Blow-out/blow-crack of general-purpose polyethylene blow molded products
문제 현상
The parison is blown out during the blow '2079851475616104453, and holes or cracks appear in the product.
Blow-out leads to product scrapping, and is usually caused by excessive blowing air pressure or parison quality problems.
원인 분석
（1）The blowing air pressure is too large, exceeding the parison's bearing capacity
（2）The parison wall thickness is uneven, and the thin-walled part is blown out first
（3）The parison temperature is too low, and the ductility is poor
（4）The blowing speed is too fast, and the parison has no time to deform uniformly
（5）There are impurities or bubbles in the parison as weak points
해결 방법
（1）Appropriately reduce the blowing air pressure to 0.3-0.6MPa
（2）Enable parison wall thickness control to ensure uniform wall thickness
（3）Appropriately raise the extrusion temperature to a reasonable value within the range of 160-260°C
（4）Use a staged blowing method of pre-blowing + high-pressure blowing
（5）Check the cleanliness of the raw material and remove impurities
핵심 요약
Blow-out is caused by excessive blowing air pressure or poor parison quality, and the blowing process and parison quality need to be optimized.