Welding joint leakage of heat-resistant polyethylene PPR pipes (Variant: strengthened measures)
문제 현상
After hot melt welding of PPR/PP-R pipes, the joints leak in the pressure test, and the weld strength is insufficient.
Welding joint leakage is a common failure point of pipeline systems and affects the safety of the water supply system.
In particular, extra attention is needed on the original basis, this problem is more prominent and needs key attention.
원인 분석
（1）The welding temperature is improper, not reaching the melting temperature of the material or too high, causing degradation
（2）The welding time is insufficient, and the depth of the surface molten layer is not enough
（3）The pipe and the fitting are not concentric during welding
（4）The welding surface is contaminated with oil, water, or dust
（5）The pipe wall thickness is uneven or the fitting diameter does not match
（6）On the original basis, extra attention is needed: process parameter fluctuations or equipment status changes have aggravated this problem
해결 방법
（1）Control the hot melt welding temperature at 260-280°C (PPR/PP-R), and strictly calibrate the heating plate temperature
（2）Strictly implement the standard welding time: 5s for DN20 pipe, 7s for DN25 pipe, etc.
（3）Use special clamping tools to ensure that the pipe and the fitting are concentric and aligned
（4）Clean the welding surfaces of the pipe and the fitting before welding to remove oil and dust
（5）Use pipes and fittings of the same brand and series to ensure dimensional matching
（6）And strengthen process monitoring; on the original basis, extra attention is needed, with special attention to parameter stability
핵심 요약
PPR welding joint leakage is caused by improper welding parameters or welding surface contamination, and the welding temperature, time, and cleanliness need to be strictly controlled.
In different production scenarios, targeted preventive measures need to be taken.