Longitudinal retraction rate of polyolefin plastomer pipes exceeding the standard
문제 현상
After the pipe is heated under the specified temperature and time conditions, the longitudinal retraction rate exceeds the standard limit.
Excessive retraction rate reflects large internal stress or incomplete crystallization of the pipe, affecting the reliability of the pipe in use.
원인 분석
（1）The residual internal stress of the polyolefin plastomer after extrusion is large
（2）The cooling rate is too fast and the molecular chain orientation has not relaxed
（3）The hauling speed is too large and the pipe is overstretched longitudinally
（4）The barrel temperature is too low and the melt plasticization is insufficient
（5）The sizing cooling is insufficient
해결 방법
（1）Appropriately raise the barrel temperature to a reasonable value within the range of 180-230°C to improve plasticization
（2）Appropriately reduce the cooling rate to allow the molecular chains time to relax
（3）Adjust the hauling speed and reduce the stretching ratio
（4）Increase the length of the cooling water tank to ensure sufficient cooling
（5）Perform water bath annealing treatment on the pipe after demolding to eliminate internal stress
핵심 요약
Excessive retraction rate is caused by large internal stress or excessive orientation, and needs to be solved from temperature control, cooling rate, and hauling speed.