Extrusion & Post
11 조회수
Blocking/Poor Opening of Polypropylene Film
문제 현상
The film layers stick together and are difficult to separate, affecting subsequent processing and use.
Poor opening is especially prominent in film winding and automatic packaging, reducing production efficiency.
원인 분석
(1) The surface tension of polypropylene film is high, and the interlayer adhesion is large
(2) The film is wound at too high a temperature, and the cooling is insufficient
(3) The winding tension is too large
(4) There is a lack of anti-blocking agent
(5) The film thickness is too thin, making blocking easier
해결 방법
(1) Add an appropriate amount of anti-blocking agent (such as silica fine powder 0.1-0.5%)
(2) Ensure the film is fully cooled before winding, and the winding temperature does not exceed 40°C
(3) Appropriately reduce the winding tension
(4) Add an appropriate amount of slip agent (such as oleamide 0.1-0.3%) to reduce surface friction
(5) Control the film thickness within a reasonable range
핵심 요약
Film blocking is caused by surface tension and temperature, and needs to be solved by adding an anti-blocking agent and controlling the winding conditions.