Injection Molding
11 조회수
Low Tensile Strength of Block Copolymer Polypropylene Injection Molded Products
문제 현상
The tensile strength test value of the product is lower than the material standard requirement, and plastic deformation or fracture easily occurs when stressed.
Low tensile strength directly affects the service life and safety performance of the product.
원인 분석
（1）The melt temperature is too high, the material thermally degrades in the barrel, and the molecular weight decreases
（2）The screw rotation speed is too fast, and shear overheating causes molecular chain breakage
（3）Too much regrind is used, and repeated thermal processing reduces the molecular weight
（4）The holding pressure is insufficient, and there are shrinkage cavities or pores inside the product
（5）The product contains impurities or the color masterbatch is unevenly dispersed, forming weak points
해결 방법
（1）Control the barrel temperature at a reasonable value within the 200-270°C range to avoid overheating
（2）Reduce the screw rotation speed to 50-100rpm to reduce shear
（3）Control the regrind ratio to no more than 20%, and fully mix the new material and the regrind
（4）Increase the holding pressure to 80-120MPa and extend the holding pressure time to ensure sufficient shrinkage compensation
（5）Check the purity of the raw material to ensure the color masterbatch and additives are uniformly dispersed
핵심 요약
Low tensile strength is mainly caused by material degradation or internal defects, and the processing temperature, shear, and regrind ratio need to be controlled.