문제 현상
Cracks appear in PETG products during storage or use, especially when contacting solvents or subjected to bending stress.
원인 분석
Molding internal stress too large (cooling too fast or mold temperature too low), stress concentration at abrupt wall thickness changes, environmental stress cracking (ESC).
해결 방법
Increase the mold temperature to 30-50°C; design the product to avoid sharp corners and abrupt wall thickness changes; anneal at 60-70°C for 2-4h.
핵심 요약
PETG environmental stress cracking sensitivity needs management from mold temperature, product design and post-processing.