문제 및 해결책

일반적인 플라스틱 재료 문제에 대한 실질적인 답변

기사 둘러보기 →

Q

PP Extrusion Melt Fracture

A

Exit roughness: raise temperature, reduce speed, apply PPA.

Extrusion & Post PP;extrusion;melt fracture;sharkskin;PPA

Q

PP Regrind-Induced Embrittlement

A

PP regrind requires 'control ratio, control heat history, control drying' simultaneously, monitored with melt index and impact data; better flowability does not equal better usability—it is often exactly the signal of molecular weight drop and performance degradation.

Material Drying PP;regrind;embrittlement;degradation;molecular weight;melt index

Q

PP '2079851475616104452 Black Speck

A

Black speck control relies on normalized dead-spot cleaning.

Injection Molding PP;black speck;carbonization;dead spot;purging

Q

PP Glass Fiber Floating Fiber

A

The core of floating fiber is 'coverage': only with temperature up and speed down can resin wrap the glass fibers; high-appearance GF parts often need the combination of process, mold texture, and grade—machine adjustment alone can hardly eradicate it completely.

Injection Molding PP;glass fiber;floating fiber;coverage;melt temperature;mold temperature

Q

PP Glass Fiber Reinforced Warpage

A

Orientation warpage is broken through from gate design.

Molds & Tooling PP;glass fiber;warpage;orientation;gate

Q

PP Part Uneven Gloss

A

Uneven gloss points to a mold temperature distribution problem; water circuit balancing modification can solve it once and for all.; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence

Molds & Tooling PP;uneven gloss;mold temperature;water circuit;crystallization;cooling

Q

PP Mold Sticking

A

For mold sticking, reduce pressure first, then fix draft and polishing.

Molds & Tooling PP;mold sticking;holding pressure;draft angle;polishing

Q

PP Ejector Whitening and Cracking

A

The main control line for PP ejector whitening/cracking is 'reduce gripping force + disperse ejection force + sufficient cooling': first extend cooling, then enlarge ejection area, finally reduce holding pressure; whitening itself is an alarm of excessive ejection force—disperse the force to elim...

Molds & Tooling PP;ejector whitening;ejection cracking;gripping force;ejection;cooling

Q

PP Part Internal Bubble

A

For PP bubbles, first distinguish 'vacuum bubble' from 'gas bubble': vacuum bubbles rely on feeding (holding pressure + gate position), gas bubbles rely on venting and volatiles control (drying + cooling + venting)—failure to distinguish leads in the opposite direction.

Material Drying PP;bubble;vacuum bubble;holding pressure;regrind;venting

Q

PP Trapped Gas Burning

A

Repeated burning at fixed positions is 90% a venting problem: first clean/open vent grooves, then adjust end speed—don't just blindly lower melt temperature; burn points are often the last-filled points of the cavity and can be precisely located with the short shot method.

Injection Molding PP;trapped gas;burnt;diesel effect;vent groove;short shot method