Problem & Solution

Practical answers to common plastic material challenges

Browse Articles →

Q

ASA building material gutter deformation

A

The thermal deformation of ASA building materials is a joint problem of material boundary and structural design; fixing point design is more economical than changing materials; the actual roof temperature far exceeds air temperature.; After confirming effectiveness, solidify the parameters and pr...

Molding Process ASA；gutter；building material；thermal deformation；sagging；expansion

Q

ASA automotive exterior part comprehensive failure

A

ASA automotive part failures are mostly multi-factor coupling; systematic investigation is better than single-point trial and error; combined condition testing is a reliable path for reproduction and verification.; After confirming effectiveness, solidify the parameters and practices into the wor...

Molding Process ASA；automotive exterior；failure；aging；vibration；FMEA

Q

AEPDS processing temperature

A

AEPDS temperature management protects EPDM rubber; actual measurement prevents deviation; residence time control.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Molding Process AEPDS; processing temperature; EPDM; degradation; plasticization; actual measurement

Q

ABS vent depth

A

ABS vent 0.025-0.05mm, shallow traps gas and deep causes flash; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar problems

Molding Process vent depth trapped gas flash

Q

ABS hopper bridging, unstable feeding

A

ABS 'if the feeding is unstable, no matter how accurate the process is, it is in vain': bridging and crushed material are common culprits; include the plasticizing time in monitoring, it often alarms before the product has problems.

Molding Process ABS；bridging；hopper；feeding；crushed material

Q

ABS granule hopper bridging

A

If the feeding is unstable, no matter how accurate the process is, it is in vain.

Molding Process ABS；bridging；hopper；feeding；crushed material

Q

ABS brittle cracking——metal insert stress

A

Insert parts need preheating, and sufficient interface wall thickness must be reserved.

Molding Process ABS；insert；stress cracking；shrinkage difference；preheating

Q

ABAK heat resistance balance

A

ABAK heat resistance is a function of the ratio; glass fiber reinforcement is the improvement means; actual measurement verification is more reliable than theoretical estimation.; After confirming effectiveness, fix the parameters and practices into the work instructions to prevent recurrence

Molding Process ABAK；heat resistance；heat deflection temperature；ratio；glass fiber；actual measurement

Q

ABAK processing temperature window

A

The ABAK temperature window is the intersection of the thermal properties of the two components; PA6-based is easier to process than PA66-based; actual measured temperature is the process benchmark.; After confirming effectiveness, fix the parameters and practices into the work instructions to pr...

Molding Process ABAK；processing temperature；window；PA6；PA66；degradation

Q

Fiber Fuzzing of Prepreg

A

This problem is a typical manifestation of fiber fuzzing of prepreg in compression molding. The core of the solution lies in the reasonable preheating of the material and the guarantee of fluidity, as well as the precise matching of mold temperature and molding pressure. It is recommended to make...

Molding Process fiber orientationglass fiber floatinggate sizemelt temperatureglass fiber content