Problem & Solution

Practical answers to common plastic material challenges

Browse Articles →

Resonance deformation of the product on high-speed filling lines

In summary, the causes of the "Resonance deformation of the product on high-speed filling lines" problem can be attributed to the combined action of multiple factors such as The natural frequency of the product is close to the vibration frequency of the filling line, Insufficient product rigidity...

Thermoforming Resonance deformation of the product on high-speed filling lines '2079851475616104458

Poor sealing between the two layers after twin-sheet '2079851475616104458

In summary, the causes of the "Poor sealing between the two layers after twin-sheet '2079851475616104458" problem can be attributed to the combined action of multiple factors such as Mismatched temperatures of the two sheets, Insufficient mold closing pressure.To solve this problem, it is necessa...

Thermoforming Poor sealing between the two layers after twin-sheet '2079851475616104458 '2079851475616104458 temperature control pressure regulation clamping accuracy

Sheet heating oven temperature controller failure causing over-temperature

In summary, the causes of the "Sheet heating oven temperature controller failure causing over-temperature" problem can be attributed to the combined action of multiple factors such as Temperature controller failure, Thermocouple damage.To solve this problem, it is necessary to start from aspects ...

Thermoforming Sheet heating oven temperature controller failure causing over-temperature '2079851475616104458 temperature control heating process

Product bumps at mold vacuum holes

In summary, the causes of the "Product bumps at mold vacuum holes" problem can be attributed to the combined action of multiple factors such as Vacuum holes too large, Excessive forming pressure.To solve this problem, it is necessary to start from aspects such as Reduce the vacuum hole size, Redu...

Thermoforming Product bumps at mold vacuum holes '2079851475616104458 pressure regulation mold design

Sheet slippage caused by uneven clamping frame pressure

In summary, the causes of the "Sheet slippage caused by uneven clamping frame pressure" problem can be attributed to the combined action of multiple factors such as Uneven clamping frame pressure, Uneven wear of the clamping surface.To solve this problem, it is necessary to start from aspects suc...

Thermoforming Sheet slippage caused by uneven clamping frame pressure '2079851475616104458 pressure regulation

Carbonized black lines on the product surface

In summary, the causes of the "Carbonized black lines on the product surface" problem can be attributed to the combined action of multiple factors such as Carbonized impurities in the sheet, Carbon deposits on the mold surface.To solve this problem, it is necessary to start from aspects such as C...

Thermoforming Carbonized black lines on the product surface '2079851475616104458 mold design surface quality

Accidental opening of the safety valve during air-pressure forming

In summary, the causes of the "Accidental opening of the safety valve during air-pressure forming" problem can be attributed to the combined action of multiple factors such as Pressure regulating valve failure, Pressure sensor failure.To solve this problem, it is necessary to start from aspects s...

Thermoforming Accidental opening of the safety valve during air-pressure forming '2079851475616104458 pressure regulation

Regular ripples on the sheet surface (elastic instability)

In summary, the causes of the "Regular ripples on the sheet surface (elastic instability)" problem can be attributed to the combined action of multiple factors such as Elastic unstable deformation of the sheet after heating.To solve this problem, it is necessary to start from aspects such as Rais...

Thermoforming Regular ripples on the sheet surface (elastic instability) '2079851475616104458 surface quality

Stress cracking occurs in the product after long-term use

In summary, the causes of the "Stress cracking occurs in the product after long-term use" problem can be attributed to the combined action of multiple factors such as Long-term action of residual stress, Acceleration by environmental factors.To solve this problem, it is necessary to start from as...

Thermoforming Stress cracking occurs in the product after long-term use '2079851475616104458 stress control

Star-shaped cracks at the bottom of the product after deep drawing

In summary, the causes of the "Star-shaped cracks at the bottom of the product after deep drawing" problem can be attributed to the combined action of multiple factors such as Excessive stretching at the bottom center, Local defects in the sheet.To solve this problem, it is necessary to start fro...

Thermoforming Star-shaped cracks at the bottom of the product after deep drawing '2079851475616104458 stretch ratio