Melt Fracture in PU Extrusion
Sorun Belirtisi
PU shows severe melt fracture at excessive extrusion rate, extrudate spirally twisted
Neden Analizi
PU melt elasticity too high, elastic recovery at the die exit exceeding the critical value; die L/D ratio too short <10, melt not fully relaxed; extrusion temperature too low
Çözüm
1) Reduce extrusion rate to 2-3m/min; 2) Increase die L/D ratio to 15-20; 3) Increase extrusion temperature to 60-120°C; 4) Add a small amount of low-elasticity resin to reduce system elasticity; 5) Gradual contraction die entrance design
Temel Çıkarım
Melt fracture is caused by elastic recovery exceeding the critical value; reducing speed and lengthening the die are the core countermeasures