The uneven film formation problem of PBAK acrylate type in emulsion polymerization
Sorun Belirtisi
Polybutyl acrylate-type PBAK exhibited uneven film formation during emulsion polymerization processing at 80-150°C.
Neden Analizi
Improper crosslinking degree of PBAK caused the problem.
Çözüm
Control crosslinking.
Temel Çıkarım
PBAK for coating and adhesive applications requires fine formulation design.