Extrusion & Post
11 görüntüleme
PPA reduces back pressure in HDPE pipe extrusion
Sorun Belirtisi
During extrusion of HDPE pipes (PE100), the die head pressure is too high (30% above the normal value), the main machine current is overloaded, the extrusion output has to be reduced by 20%, and production efficiency is severely limited.
Neden Analizi
HDPE PE100 has a high molecular weight (MFR 0.2-0.3 g/10min) and high melt viscosity, resulting in high die head resistance; PPA is not used or the PPA molecular weight does not match HDPE; the die flow channel design is narrow (the L/D ratio is too large); the processing temperature is too low and melt flowability is limited.
Çözüm
Add 0.03-0.06% PPA to the HDPE pipe formulation to reduce melt/metal wall friction; select a high molecular weight PPA grade (Mw 500,000+) to ensure coating durability; optimize the die flow channel design to reduce the L/D ratio; appropriately raise the processing temperature by 5-10°C (within the material's temperature resistance range).
Temel Çıkarım
By reducing melt/metal friction, PPA can significantly reduce the die head pressure and energy consumption of large pipe extrusion.