Cross-linked polyethylene pipe longitudinal reversion rate exceeding standard (Variant: strengthened measures)
Sorun Belirtisi
After the pipe is heated under specified temperature and time conditions, the longitudinal reversion rate exceeds the standard limit.
Excessive reversion rate reflects large internal stress or imperfect crystallization of the pipe, affecting the reliability of pipe use.
Especially on the original basis, additional attention is needed, and this problem is more prominent and requires key attention.
Neden Analizi
(1) Large residual internal stress after cross-linked polyethylene extrusion
(2) Cooling rate too fast, molecular chain orientation not relaxed
(3) Haul-off speed too large, pipe excessively stretched longitudinally
(4) Barrel temperature too low, melt plasticization insufficient
(5) Sizing cooling insufficient
(6) On the original basis, additional attention is needed: process parameter fluctuations or equipment state changes aggravate this problem
Çözüm
(1) Appropriately increase barrel temperature to a reasonable value within 170-220°C to improve plasticization
(2) Appropriately reduce cooling rate to give molecular chains relaxation time
(3) Adjust haul-off speed, reduce draw ratio
(4) Increase cooling water tank length to ensure sufficient cooling
(5) After pipe demolding, perform water bath annealing to eliminate internal stress
(6) And strengthen process monitoring; on the original basis, additional attention is needed, paying special attention to parameter stability
Temel Çıkarım
Excessive reversion rate is caused by large internal stress or excessive orientation, and needs to be solved from temperature control, cooling rate and haul-off speed.
Targeted preventive measures need to be taken in different production scenarios.