Sorun ve Çözüm

Q

Sink Marks at Thick-Wall Sections of High-Density Polyethylene Injection-Molded Products

A

Sink marks are a typical defect in the '2079851475616104452 of crystalline materials; the root cause is that local volume shrinkage is not effectively compensated, and it needs to be solved coordinately from three aspects: holding parameters, gate design, and cooling conditions.

Injection Molding sink markholding pressurecrystallization shrinkagegate designuniform wall thickness

2 görüntüleme

Tam Yanıtı Oku →

Q

Weld Lines on High-Density Polyethylene Injection-Molded Products (Variant: Strengthened Measures)

A

Weld lines are a manifestation of poor melt convergence and fusion; the melt fusion quality is improved by increasing the melt temperature, injection speed, and mold temperature. Targeted preventive measures need to be taken in different production scenarios.

Injection Molding weld linemelt convergenceinjection speedmold temperaturegate design

2 görüntüleme

Tam Yanıtı Oku →

Q

Sink Marks at Thick-Wall Sections of High-Density Polyethylene Injection-Molded Products (Variant: Strengthened Measures)

A

Sink marks are a typical defect in the '2079851475616104452 of crystalline materials; the root cause is that local volume shrinkage is not effectively compensated, and it needs to be solved coordinately from three aspects: holding parameters, gate design, and cooling conditions. Targeted preventi...

Injection Molding sink markholding pressurecrystallization shrinkagegate designuniform wall thickness

2 görüntüleme

Tam Yanıtı Oku →

Q

Cracking of Biaxially Oriented Polypropylene Film Products Caused by Internal Stress

A

Internal stress cracking is a manifestation of processing stress exceeding the strength of the material.

Injection Molding internal stressstress crackinginjection speedmold temperatureuniform wall thickness

2 görüntüleme

Tam Yanıtı Oku →

Q

Thread Stripping of PVDF Injection-Molded Parts

A

Thread design requires special consideration

Injection Molding PVDFthread

2 görüntüleme

Tam Yanıtı Oku →

Q

PVDF injection cycle is too long, affecting efficiency

A

Cycle optimization is the key to increasing production and reducing cost

Injection Molding PVDFmolding cycle

2 görüntüleme

Tam Yanıtı Oku →

Q

Flowability decline after glass fiber reinforcement

A

A trade-off between reinforcement effect and processability is needed

Injection Molding PVDFglass fiber

2 görüntüleme

Tam Yanıtı Oku →

Q

Burnt yellow spots on injection molded products

A

Thermal decomposition produces HF and must be strictly avoided

Injection Molding PVDFburnt yellow

2 görüntüleme

Tam Yanıtı Oku →

Q

Stress corrosion cracking of pump casings

A

Annealing is an effective means to eliminate stress

Injection Molding PVDFpump casing

2 görüntüleme

Tam Yanıtı Oku →

Q

Abnormal injection melt viscosity

A

The processing temperature window is narrow and the operation requirements are high

Injection Molding PVDFviscosity

2 görüntüleme

Tam Yanıtı Oku →