2025 soru
Q
Improper processing temperature window selection for low density polyethylene low density polyethylene
A
Temperature window selection is the foundation of processing; it needs to be reasonably set according to material characteristics and practical operation experience.
Processing Machinery processing temperaturetemperature windowplasticizing qualitymaterial degradationtemperature calibration
2 görüntüleme
Tam Yanıtı Oku →
Q
Poor thermal stability of low density polyethylene raw material causing degradation during processing
Q
Uneven Cutting End Face of High-Density Polyethylene Pipes
A
An uneven cutting end face is caused by tool wear or improper cutting parameters, and the tool needs to be maintained and the cutting process optimized.
Processing Machinery cutting end facecutting toolcutting speedpipe coolingcutting machine correction
2 görüntüleme
Tam Yanıtı Oku →
Q
Excessive Gel/Gel Particles in High-Density Polyethylene Extruded Products
Q
Pressure Resistance Test Failure of High-Density Polyethylene Pipes
A
Pressure resistance failure is caused by insufficient wall thickness, material degradation, or internal defects, and needs to be systematically solved from process and material quality.
Processing Machinery pressure resistance testpipe wall thicknessmaterial degradationcrystallinityplasticization quality
2 görüntüleme
Tam Yanıtı Oku →
Q
Large Current Fluctuation of High-Density Polyethylene Extruder
A
Current fluctuation is caused by large plasticization resistance or equipment problems, and needs to be solved from temperature control, raw material purity, and equipment maintenance.
Processing Machinery current fluctuationscrew torqueplasticizing temperatureraw material impuritiesfilter screen clogging
2 görüntüleme
Tam Yanıtı Oku →
Q
Poor Plasticization Caused by Screw Wear of High-Density Polyethylene Extruder
A
Screw wear leads to decreased plasticization efficiency, and needs to be solved by selecting wear-resistant materials and regular maintenance.
Processing Machinery screw wearpoor plasticizationwear-resistant materialscrew gapscrew rotation speed
2 görüntüleme
Tam Yanıtı Oku →
Q
Large Barrel Temperature Fluctuation During Processing of High-Density Polyethylene High-Density Polyethylene
Q
Wide Temperature Window of High-Density Polyethylene PE Raw Material Causing Difficulty in Process Parameter Optimization
A
PE temperature window optimization needs to be advanced from two aspects: systematic experiments and experience accumulation.
Processing Machinery temperature optimizationPE gradeDOEprocess parameterstemperature database
2 görüntüleme
Tam Yanıtı Oku →
Q
Frequent Screen Change/Short Filter Screen Life of High-Density Polyethylene Extruder