Sorun ve Çözüm

Yaygın plastik malzeme zorluklarına pratik yanıtlar

Makalelere Göz At →

ABS brittle cracking——metal insert stress

Insert parts need preheating, and sufficient interface wall thickness must be reserved.

Molding Process ABS；insert；stress cracking；shrinkage difference；preheating

16 görüntüleme

Tam Yanıtı Oku →

ABS brittle cracking——too low mold temperature, weak weld line

Weld line strength is guaranteed by temperature; low temperature and fast cooling is an invisible killer.

Molds & Tooling ABS；brittle cracking；weld line；mold temperature；molecular entanglement

9 görüntüleme

Tam Yanıtı Oku →

ABS brittle cracking——too small gate shear overheating

A small gate saves material but may exchange for brittle parts: the shear heat and internal stress at the gate are hidden killers; if appearance allows, making the gate a little bigger often solves local brittleness better than adjusting a bunch of parameters.

Molds & Tooling ABS；brittle cracking；gate；shear heat；internal stress

9 görüntüleme

Tam Yanıtı Oku →

ABS product brittle cracking——ejection system imbalance

For ABS ejection cracking, check the ejection mechanism first rather than the material: balancing the ejection force, increasing the load-bearing area, and giving sufficient cooling are the three axes; the ejection cracking location is often the ejector pin location, and following the ejector pin...

Molds & Tooling ABS；ejection cracking；ejection；stress concentration；ejector pin；cooling

9 görüntüleme

Tam Yanıtı Oku →

ABS product brittle cracking——excessive regrind ratio

ABS regrind is not unusable, but the ratio and thermal history must be controlled; the improvement in fluidity is precisely a signal of molecular weight decrease; don't be fooled by 'easy to mold'——the performance account must be calculated with impact and tensile data.

Material Drying ABS；brittle cracking；regrind ratio；molecular weight；regenerated material

9 görüntüleme

Tam Yanıtı Oku →

ABS product brittle cracking——plasticizing capacity mismatch

Matching the ABS plasticizing capacity with the product is the first equipment gate against brittleness: too large or too small both cause brittleness; factoring in 'residence time' when selecting the machine is far more effective than adjusting the process on the wrong machine afterwards.

Injection Molding ABS；brittle cracking；plasticizing capacity；residence time；machine matching

16 görüntüleme

Tam Yanıtı Oku →

ABS product brittle cracking——barrel dead corner degradation

For chronic, widespread brittleness of ABS, prioritize suspecting equipment dead corner degradation rather than the process; purging and disassembling and cleaning dead corners is the fundamental cure; repeatedly adjusting the process on equipment with dead corners only wastes material and covers...

Molds & Tooling ABS；brittle cracking；degradation；barrel dead corner；purging

9 görüntüleme

Tam Yanıtı Oku →

ABS vacuum void (shrinkage cavity)

For ABS bubbles, first distinguish 'vacuum void' from 'gas-containing bubble': bubbles that exist the moment the mold opens are mostly gas-containing (moisture), those that appear later inside are mostly vacuum voids; vacuum voids rely on compensation, gas-containing bubbles rely on venting; only...

Material Drying ABS；vacuum void；shrinkage cavity；holding pressure；compensation；thick wall

9 görüntüleme

Tam Yanıtı Oku →

Internal bubbles in products caused by ABS water content

For bubbles, check water content first, then check temperature and venting; the order cannot be reversed.

Material Drying ABS；bubbles；moisture；drying；back pressure

9 görüntüleme

Tam Yanıtı Oku →

Silver streaks (material bloom) caused by insufficient ABS raw '2079851475616104451

More than 90% of ABS silver streaks are moisture problems; check drying first before adjusting the process; water content not only produces silver streaks, but also catalyzes degradation and makes the product brittle, so drying is both an appearance gate and a performance gate, and must be manage...

Material Drying ABS；silver streak；material bloom；drying；moisture content；catalytic cracking

9 görüntüleme

Tam Yanıtı Oku →

Önceki 1 ... 1038 1039 1040 1041 1042 1043 1044 ... 1164 Sonraki

Kategoriler

Tüm Konular 11636 Material Drying 1439 Injection Molding 1506 Molding Process 740 Molds & Tooling 1506 Processing Machinery 2025 Extrusion & Post 2239 Blow Molding 315 Thermoforming 141 Material Analysis 1343 Production & Quality 382

Sorun ve Çözüm

Kategoriler

Teklif Al