Sorun ve Çözüm

Yaygın plastik malzeme zorluklarına pratik yanıtlar

Makalelere Göz At →

Uneven Density Distribution of PTFE Raw Material Tape Produced by Calendering Process

This problem is a typical manifestation of uneven density distribution of PTFE raw material tape produced by calendering process in calendering. The core of the solution lies in the precise adjustment of nip compensation, uniform control of roll temperature distribution, and stability assurance o...

Extrusion & Post uneven roll temperatureheat transfer oil channelsroll end heat dissipationinfrared temperature measurementtemperature control deviation

16 görüntüleme

Tam Yanıtı Oku →

Annular Airflow Interference Between Rolls of Ultra-thin Calendered Films (<20μm)

This problem is a typical manifestation of annular airflow interference between rolls of ultra-thin calendered films (<20μm) in calendering. The core of the solution lies in the precise adjustment of nip compensation, uniform control of roll temperature distribution, and stability assurance of th...

Extrusion & Post roll surface wearhard impuritiesnatural wearroll surface protectionmetal detection

16 görüntüleme

Tam Yanıtı Oku →

Light Transmittance Attenuation of Photovoltaic EVA Encapsulation Film After Embossing

This problem is a typical manifestation of light transmittance attenuation of photovoltaic EVA encapsulation film after embossing in calendering. The core of the solution lies in the precise adjustment of nip compensation, uniform control of roll temperature distribution, and stability assurance ...

Extrusion & Post light transmittance attenuation of photovoltaic EVA encapsulation film after embossingtemperaturepressure

16 görüntüleme

Tam Yanıtı Oku →

Ultra-high Shear at the Nip Causing Polymer Chain Scission

This problem is a typical manifestation of ultra-high shear at the nip causing polymer chain scission in calendering. The core of the solution lies in the precise adjustment of nip compensation, uniform control of roll temperature distribution, and stability assurance of the feed system. It is re...

Extrusion & Post uneven roll temperatureheat transfer oil channelsroll end heat dissipationinfrared temperature measurementtemperature control deviation

16 görüntüleme

Tam Yanıtı Oku →

Roll Thermal Shock at the Moment of Power Failure of the Calendering Line

This problem is a typical manifestation of roll thermal shock at the moment of power failure of the calendering line in calendering. The core of the solution lies in the precise adjustment of nip compensation, uniform control of roll temperature distribution, and stability assurance of the feed s...

Extrusion & Post uneven roll temperatureheat transfer oil channelsroll end heat dissipationinfrared temperature measurementtemperature control deviation

16 görüntüleme

Tam Yanıtı Oku →

Misalignment During Film Folding Caused by Film Static Electricity

This problem is a typical manifestation of misalignment during film folding caused by film static electricity in calendering. The core of the solution lies in the precise adjustment of nip compensation, uniform control of roll temperature distribution, and stability assurance of the feed system. ...

Extrusion & Post spinning static electricityambient humiditystatic eliminationantistatic agentyarn guide material

16 görüntüleme

Tam Yanıtı Oku →

Local Corrosion Pits on the Calender Roll Surface (Chloride Ion Corrosion)

This problem is a typical manifestation of local corrosion pits on the calender roll surface (chloride ion corrosion) in calendering. The core of the solution lies in the precise adjustment of nip compensation, uniform control of roll temperature distribution, and stability assurance of the feed ...

Extrusion & Post roll surface wearhard impuritiesnatural wearroll surface protectionmetal detection

16 görüntüleme

Tam Yanıtı Oku →