Bubbles around inserts

The three major causes of bubbles (moisture, air entrapment, vacuum shrinkage cavities) need to be treated differently: moisture type——sufficient drying; air entrapment type——optimize plasticization and injection parameters; vacuum shrinkage cavity type——strengthen holding pressure feeding. Accur...

Material Drying bubblesraw '2079851475616104451back pressure controlvacuum shrinkage cavitymold venting

10 görüntüleme

Tam Yanıtı Oku →

Uneven thickness

This problem is a typical manifestation of uneven thickness in compression molding; the core of the solution lies in proper preheating of the material and assurance of flowability, as well as precise matching of mold temperature and molding pressure. It is recommended to adjust coordinately from ...

Molds & Tooling feeding amountmaterial flowabilityweighing accuracyhopper bridgingmaterial distribution

3 görüntüleme

Tam Yanıtı Oku →

Embrittlement

The essence of embrittlement is that the material's toughness reserve declines to the point of being unable to meet use requirements. The control key is the 'three temperatures'——processing temperature (avoid excessive degradation), drying temperature (avoid too low leaving residual moisture and ...

Material Analysis embrittlementthermal degradationdrying conditionsregrind ratioimpact strength

10 görüntüleme

Tam Yanıtı Oku →

Insufficient strength

This problem is a typical manifestation of insufficient strength in compression molding; the core of the solution lies in proper preheating of the material and assurance of flowability, as well as precise matching of mold temperature and molding pressure. It is recommended to adjust coordinately ...

Material Drying curing degreecatalyst dosagemold temperaturecuring timepost-curing

8 görüntüleme

Tam Yanıtı Oku →

Demolding cracks

This problem is a typical manifestation of demolding cracks in compression molding; the core of the solution lies in proper preheating of the material and assurance of flowability, as well as precise matching of mold temperature and molding pressure. It is recommended to adjust coordinately from ...

Molds & Tooling draft anglemold polishingholding pressurecooling timerelease agent

3 görüntüleme

Tam Yanıtı Oku →

Difficult demolding/mold sticking

This problem is a typical manifestation of difficult demolding/mold sticking in compression molding; the core of the solution lies in proper preheating of the material and assurance of flowability, as well as precise matching of mold temperature and molding pressure. It is recommended to adjust c...

Molds & Tooling draft anglemold polishingholding pressurecooling timerelease agent

3 görüntüleme

Tam Yanıtı Oku →

Warpage deformation

Warpage is the macroscopic bending caused by inconsistent shrinkage of various parts of the product. The solution idea is: achieve uniform cooling of all parts during the cooling stage (cooling water channel optimization), adopt symmetrical layout and isotropic design in structural design (wall t...

Molds & Tooling warpage deformationcooling uniformityresidual stressgate symmetryannealing

3 görüntüleme

Tam Yanıtı Oku →

Uneven shrinkage

This problem is a typical manifestation of uneven shrinkage in compression molding; the core of the solution lies in proper preheating of the material and assurance of flowability, as well as precise matching of mold temperature and molding pressure. It is recommended to adjust coordinately from ...

Injection Molding shrinkage ratewall thickness designcooling water channelsholding pressuredimensional accuracy

8 görüntüleme

Tam Yanıtı Oku →

Pitting/pinholes

This problem is a typical manifestation of pitting/pinholes in compression molding; the core of the solution lies in proper preheating of the material and assurance of flowability, as well as precise matching of mold temperature and molding pressure. It is recommended to adjust coordinately from ...

Material Drying draft anglemold polishingholding pressurecooling timerelease agent

7 görüntüleme

Tam Yanıtı Oku →

Flow lines/flow marks

This problem is a typical manifestation of flow lines/flow marks in compression molding; the core of the solution lies in proper preheating of the material and assurance of flowability, as well as precise matching of mold temperature and molding pressure. It is recommended to adjust coordinately ...

Molds & Tooling flow marksmelt temperaturemold temperatureinjection speedripples

3 görüntüleme

Tam Yanıtı Oku →

Önceki 1 ... 1150 1151 1152 1153 1154 1155 1156 ... 1164 Sonraki

Kategoriler

Tüm Konular 11636 Material Drying 1439 Injection Molding 1506 Molding Process 740 Molds & Tooling 1506 Processing Machinery 2025 Extrusion & Post 2239 Blow Molding 315 Thermoforming 141 Material Analysis 1343 Production & Quality 382

Sorun ve Çözüm

Kategoriler

Teklif Al