Sorun ve Çözüm

Yaygın plastik malzeme zorluklarına pratik yanıtlar

Makalelere Göz At →
11636 soru
Q
Narrow processing temperature window of high impact polystyrene MSAN products
A
MSAN's narrow processing temperature window requires precise temperature control.
Processing Machinery temperature windowMSANtemperature control accuracyscrew rotation speedthermal stability
9 görüntüleme
Tam Yanıtı Oku →
Q
Quality fluctuation caused by regrind use of high impact polystyrene
A
Regrind use needs to control ratio and number of times; classified management is key.
Material Analysis regrindquality fluctuationmolecular weight decreaseregrind ratioclassified management
9 görüntüleme
Tam Yanıtı Oku →
Q
Cracking caused by internal stress of high impact polystyrene products
A
Internal stress cracking is a manifestation of processing stress exceeding material strength.
Injection Molding internal stressstress crackinginjection speedmold temperatureuniform wall thickness
9 görüntüleme
Tam Yanıtı Oku →
Q
Dimensional change with temperature/thermal expansion of high impact polystyrene products
A
Thermal expansion is an inherent material characteristic; temperature effects need to be considered in design.
Production & Quality thermal expansiondimensional changetemperature effectthermal expansion coefficientdesign compensation
9 görüntüleme
Tam Yanıtı Oku →
Q
Decreased transparency/yellowing of high impact polystyrene SAN/AS products
A
SAN transparency decrease is caused by thermal degradation or microbubbles.
Material Drying transparencyyellowingSANthermal degradationraw '2079851475616104451
9 görüntüleme
Tam Yanıtı Oku →
Q
Storage cracking/delayed cracking of high impact polystyrene PS products
A
PS delayed cracking is caused by slow release of residual stress.
Molds & Tooling delayed crackingresidual stressannealing treatmentuniform wall thicknessmold temperature
9 görüntüleme
Tam Yanıtı Oku →
Q
Rubber migration/exudation of high impact polystyrene HIPS products
A
HIPS rubber exudation is caused by compatibility and temperature.
Extrusion & Post rubber migrationexudationHIPScompatibilityprocessing temperature
9 görüntüleme
Tam Yanıtı Oku →
Q
Performance decline caused by thermal degradation of high impact polystyrene material
A
Thermal degradation is the main risk in processing; controlling temperature and reducing residence time are key.
Processing Machinery thermal degradationmolecular weight decreasebarrel temperatureresidence timescrew rotation speed
9 görüntüleme
Tam Yanıtı Oku →
Q
Shrinkage rate prediction deviation of high impact polystyrene products
A
Shrinkage rate prediction needs to be comprehensively determined in combination with material characteristics, product structure, and process parameters.
Molds & Tooling shrinkage ratemold designwall thickness effectflow directiontrial mold verification
9 görüntüleme
Tam Yanıtı Oku →
Q
Creep deformation of high impact polystyrene products
A
Creep is the slow deformation of amorphous materials under continuous load.
Material Analysis creepcontinuous loadwall thickness designmolecular weightglass fiber reinforcement
9 görüntüleme
Tam Yanıtı Oku →