Insufficient strength

The mechanical properties of the product are below standard. When this defect appears in products of Process No. 3, it is usually related to a specific process parameter range or equipment state. If it continues to appear, it will directly affect the product qualification rate and production rhythm, increasing material loss and rework costs. Timely diagnosis and elimination is a basic requirement for ensuring stable production.

1. Process parameter factors: incomplete curing, high material moisture content, insufficient molding pressure, wrong material ratio, insufficient fiber content. 2. Preheating factor: The preheating temperature and time of the material (especially thermosetting molding compounds) directly affect its flowability and curing behavior; improper preheating will lead to poor filling or uneven curing, and it is a key control point unique to compression molding.

1. Process parameter optimization and adjustment: ensure complete curing, fully dry the material, increase the molding pressure, verify the material ratio, increase the fiber content. 2. Systematic troubleshooting method: Troubleshooting of compression molding problems follows the order of 'material -> temperature -> pressure -> mold'. First check the preheating and flowability of the material, then verify the mold temperature distribution and curing time, then adjust the molding pressure and mold closing speed, and finally check the mold venting and demolding conditions. 3. Preventive management: Establish standardized process parameter cards and quality control limits for each set of mold/product, and regularly conduct process capability index (CPK) evaluations. For recurring problems, use fishbone diagrams or 5Why analysis to trace the root cause, and solidify the countermeasures as PFMEA control points.

This problem is a typical manifestation of insufficient strength in compression molding; the core of the solution lies in proper preheating of the material and assurance of flowability, as well as precise matching of mold temperature and molding pressure. It is recommended to adjust coordinately from both aspects of material state and process parameters.