PTFE Cracking and Fracture
ظاهرة المشكلة
PTFE parts develop cracks or fractures, structural integrity is lost, and failure risk under load increases.
تحليل الأسباب
Rapid cooling after sintering generates internal stress; mechanical stress overload during machining or handling; too high content of fillers such as glass fiber, carbon fiber, and bronze makes the material brittle; dropping or bending causes cracks in the semi-crystalline structure.
الحل
①Anneal after sintering to release internal stress; ②Handle carefully during post-processing and transportation; ③Optimize filler content and type to maintain toughness; ④Use appropriate tooling for machining to avoid excessive cutting force.
الخلاصة الأساسية
PTFE cracking requires cooling management, filler balance, and handling protection together; filler reinforcement and toughness trade off against each other; machining force control is a detail.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
هل كان هذا مفيدًا؟
0 شخص وجدوا هذا مفيدًا
شكرًا لك على ملاحظاتك!