Injection Molding
8 مشاهدة
PVC Injection Weak Weld Line
ظاهرة المشكلة
Cracking at weld line, insufficient strength.
تحليل الأسباب
PVC melt has high elasticity, flow front convergence temperature insufficient; degraded flow front even weaker; poor venting entrapping gas further weakens it; during on-site troubleshooting, verify item by item according to this mechanism, avoid blindly adjusting the machine based solely on experience.
الحل
①Raise temperature and speed; ②Vent at convergence; ③Adjust gate position/number, change flow direction and convergence position; ④Prevent degradation; ⑤Set overflow wells at convergence to lead cold flow front out of the cavity.
الخلاصة الأساسية
PVC weld line = 'temperature + venting + anti-degradation': PVC melt has high elasticity and converges with difficulty, temperature and venting must be given sufficiently, and more importantly prevent degraded flow front from making the weld line brittle.