Extrusion & Post
9 مشاهدة
Metallocene linear low density polyethylene film blocking/poor opening
ظاهرة المشكلة
The film layers stick together and are difficult to separate, affecting subsequent processing and use.
Poor opening is particularly prominent in film winding and automatic packaging, reducing production efficiency.
تحليل الأسباب
（1） Metallocene linear low density polyethylene film has high surface tension and large interlayer adhesion\
（2） Film wound up at too high temperature, cooling insufficient\
（3） Winding tension too large\
（4） Lack of anti-blocking agent\
（5） Film thickness too thin, more prone to blocking
الحل
（1） Add an appropriate amount of anti-blocking agent （such as silica fine powder 0.1-0.5%）\
（2） Ensure the film is fully cooled before winding, winding temperature not exceeding 40°C\
（3） Appropriately reduce winding tension\
（4） Add an appropriate amount of slip agent （such as oleamide 0.1-0.3%） to reduce surface friction\
（5） Control film thickness within a reasonable range
الخلاصة الأساسية
Film blocking is caused by surface tension and temperature, and needs to be solved by adding anti-blocking agents and controlling winding conditions.