Excessive Longitudinal Reversion Rate of Block Copolymer Polypropylene Pipes
ظاهرة المشكلة
After the pipe is heated under specified temperature and time conditions, the longitudinal reversion rate exceeds the standard limit.
Excessive reversion rate reflects large internal stress or incomplete crystallization of the pipe, affecting the reliability of pipe use.
تحليل الأسباب
（1）The residual internal stress of block copolymer polypropylene after extrusion is large
（2）The cooling rate is too fast, and the molecular chain orientation is not relaxed
（3）The haul-off speed is too large, and the pipe is excessively stretched in the longitudinal direction
（4）The barrel temperature is low, and the melt plasticization is insufficient
（5）The sizing cooling is insufficient
الحل
（1）Appropriately increase the barrel temperature to a reasonable value within the 200-270°C range to improve plasticization
（2）Appropriately reduce the cooling rate to give the molecular chains time to relax
（3）Adjust the haul-off speed to reduce the draw ratio
（4）Increase the length of the cooling water tank to ensure sufficient cooling
（5）After demolding, perform water bath annealing on the pipe to eliminate internal stress
الخلاصة الأساسية
Excessive reversion rate is caused by large internal stress or excessive orientation, and needs to be solved from temperature control, cooling rate, and haul-off speed.