Product cracking upon dropping

During the injection '2079851475616104457 production process, the product exhibits the quality defect of "Product cracking upon dropping". Specifically manifested as the product breaking in the drop test. This defect is relatively common when processing materials such as PET, PP, HDPE, and PS, and its occurrence conditions are usually related to unreasonable settings of injection pressure, parison temperature, blowing air pressure, and mold temperature. When the Product cracking upon dropping situation is severe, it will cause a series of chain-reaction quality defects in the product in terms of appearance, dimensional accuracy, mechanical properties, etc., which not only reduces the usability and safety of the product, but also directly increases the scrap rate and production cost. Therefore, this problem requires systematic diagnosis and optimization from multiple dimensions, including material selection, the condition of the injection '2079851475616104457 machine, core rod, parison mold, blow mold, and transfer mechanism, as well as injection pressure, parison temperature, blowing air pressure, and mold temperature.

1. Low strength at the weld line. The mechanical properties of the material and the structural strength of the product directly determine the safety and reliability of the product in use. The root of insufficient strength may come from factors such as the intrinsic properties of the material, degradation caused by processing, poor welding, and stress concentration caused by uneven wall thickness. Improving strength requires coordinated improvements in material selection, process optimization, and structural design. 2. Uneven wall thickness causing stress concentration. The uniformity of wall thickness distribution is directly related to the mechanical properties of the product and the consistency of cooling shrinkage. Excessive wall thickness differences will cause inconsistent cooling rates, with sink marks and warpage occurring in thick-walled areas and insufficient strength in thin-walled areas. Wall thickness design should follow the principle of uniform wall thickness, and wall thickness changes should transition smoothly. 3. Insufficient resin toughness. The selection and handling of materials is the foundation of molding quality. The intrinsic characteristics of the resin, such as molecular weight, molecular weight distribution, and melt index, determine its processing window and final performance. Factors such as excessive moisture content of the raw material, mixing in of impurities, and improper proportion of regrind will all trigger various defects during processing. In terms of equipment maintenance, inadequate regular overhaul and accuracy confirmation of the injection '2079851475616104457 machine, core rod, parison mold, blow mold, and transfer mechanism cause the actual operating parameters of the equipment to deviate from the process requirements, which can also become a potential inducement of the Product cracking upon dropping problem.

1. Reduce weld lines. Adjustments should follow the principle of gradual progress; the magnitude of each adjustment should not be too large, and it is recommended to decrease in steps of 5%~15% of the current value. After each adjustment, observe the product quality changes stably for at least 5~10 mold cycles, and continue adjusting only after confirming that the improvement direction is correct; one-step excessive adjustment must be avoided. 2. Improve wall thickness uniformity. Optimization work must be based on an accurate diagnosis of the root cause of the problem, and blind attempts must be avoided. It is recommended to first determine the key influencing factors and their interactions through the process DOE test method or historical production data analysis, and then carry out targeted parameter optimization and structural improvement to achieve twice the result with half the effort. 3. Select a high-toughness resin. Before introducing new tools, new materials, or new methods, a full applicability assessment and small-batch verification should be carried out. It is recommended to first conduct offline tests or simulation analysis outside of production conditions, and introduce them into the formal production line only after confirming effectiveness and safety. Keep change management records to facilitate subsequent traceability and experience accumulation. In terms of material management, incoming inspection of raw materials and in-process inspection of work-in-progress should be strengthened, and the key performance indicators of PET, PP, HDPE, and PS should be strictly controlled to ensure the stability of molding quality from the source.

In summary, the causes of the "Product cracking upon dropping" problem can be attributed to the combined action of multiple factors such as low strength at the weld line and uneven wall thickness causing stress concentration. Solving this problem requires starting from aspects such as reduce weld lines and improve wall thickness uniformity, and adopting systematic governance measures. In actual production, it is recommended to establish a prevention and rapid response mechanism for this problem, achieving stable production and continuous improvement through parison wall thickness uniformity and transfer temperature control.