Molds & Tooling
4 Aufrufe
Boundary of PPO Hot Mold for Stress Reduction
Problembeschreibung
【Problem Phenomenon】Using a 110-150℃ hot mold to reduce PPO stress, at higher temperatures bubbles form instead and the cycle lengthens
Ursachenanalyse
A 110-150℃ hot mold can minimize PPO stress, reduce roughness and fill thin walls; but hot mold temperature should not exceed 150℃, otherwise bubbles easily form and the cycle is extended
Lösung
Set hot mold at 110-150℃; do not exceed the 150℃ upper limit; thick-walled parts are matched with extended cooling to balance the cycle; after adjustment, continuously sample to verify the effect, and resume mass production after confirming stability
Wichtigste Erkenntnis
PPO hot mold 110-150℃ reduces stress; above 150℃ the loss outweighs the gain; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence