Defects caused by insufficient drying before cross-linked polyethylene cross-linked polyethylene processing (Variant: strengthened measures)
Problembeschreibung
Silver streaks, bubbles and rough surface appear on the product surface, and mechanical properties decrease.
The consequences of insufficient drying cover multiple defect types and are a common problem in plastics processing.
Especially on the original basis, additional attention is needed, and this problem is more prominent and requires key attention.
Ursachenanalyse
(1) Raw material absorbs moisture (although cross-linked polyethylene has low water absorption, long-term exposure still absorbs water)
(2) Drying temperature too low or drying time insufficient
(3) Drying equipment failure or insufficient dehumidification capacity
(4) Dried raw material left in humid environment too long and re-absorbs moisture
(5) Regrind not dried or insufficiently dried
(6) On the original basis, additional attention is needed: process parameter fluctuations or equipment state changes aggravate this problem
Lösung
(1) Use a dehumidifying dryer, drying temperature 60-80°C, time 2-4h
(2) Control moisture content below 0.02% after drying (cross-linked polyethylene)
(3) Seal and store raw materials after drying, cover the hopper, exposure to air not exceeding 2h
(4) Dry regrind the same as new material
(5) Control workshop ambient humidity below 60%
(6) And strengthen process monitoring; on the original basis, additional attention is needed, paying special attention to parameter stability
Wichtigste Erkenntnis
Insufficient drying is a common root cause of processing defects, and a complete drying system and moisture content detection system needs to be established.
Targeted preventive measures need to be taken in different production scenarios.