B432/E ABS
Good Heat Resistance, High Stretch, Profile Grade
Eastech
China
1 Tonne MOQ
7-14 Tage
Produkteigenschaften
Produkttyp
Raw Material
Kategorie
ABS
CAS-Nr.
9003-56-9
Hersteller
Eastech
Typ
B432/E
Herkunft
China
Farbe
Natural
Verpackung
25.00/KG Standard Packaging
Usage level
Car Part
Feature level
High Strength
Import
NO
Shape
Particle
Processing Method
Injection Molding
TDS — Technisches Datenblatt
Physical Property
| Eigenschaft | Wert | Standard | Methode |
|---|---|---|---|
| Density | 1.04 g/cm³ | 23℃ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 5.5 g/10min | 220℃ 10kg | ISO 1133 |
| Molding Shrinkage | 0.4~0.7 % | 23℃ | ISO 294/4 |
Mechanical Properties
| Eigenschaft | Wert | Standard | Methode |
|---|---|---|---|
| Tensile Strength at Yield | 48 MPa | 50mm/min | ISO 527 |
| Tensile Elongation at Break | 15 % | 50mm/min | ISO 527 |
| Tensile Modulus | 2300 MPa | 1mm/min | ISO 527 |
| Flexural Strength | 75 Mpa | 2mm/min | ISO 178 |
| Flexural Modulus | 2300 MPa | 2mm/min | ISO 178 |
| Notched Izod Impact Strength | 19 kJ/m² | 23℃,5.5J | ISO 180/1A |
Thermal properties
| Eigenschaft | Wert | Standard | Methode |
|---|---|---|---|
| Vicat Softening Temperature | 102 ℃ | 50N, 50℃/h | ISO 306 |
| Heat Distortion Temperature | 82 ℃ | 1.8MPa | ISO 75-2/A |
Die auf dieser Website bereitgestellten Lieferanten- und Produkttyp-Informationen dienen ausschließlich der branchenbezogenen Indexreferenz. Wir sind kein offizieller Vertreter einer Drittanbieter-Marke, und die angezeigten Inhalte stellen weder ein Verkaufsangebot noch ein Agenturverhältnis dar. Produktauthentizität, Preise und Verfügbarkeit unterliegen dem tatsächlichen Lieferanten.