B432/E ABS
Good Heat Resistance, High Stretch, Profile Grade
Eastech
China
MOQ de 1 tonelada
7-14 dias
Características do produto
Tipo de produto
Raw Material
Categoria
ABS
N.º CAS
9003-56-9
Fabricante
Eastech
Gama
B432/E
Origem
China
Cor
Natural
Embalagem
25.00/KG Standard Packaging
Usage level
Car Part
Feature level
High Strength
Import
NO
Shape
Particle
Processing Method
Injection Molding
TDS — Ficha técnica
Physical Property
| Propriedade | Valor | Norma | Método |
|---|---|---|---|
| Density | 1.04 g/cm³ | 23℃ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 5.5 g/10min | 220℃ 10kg | ISO 1133 |
| Molding Shrinkage | 0.4~0.7 % | 23℃ | ISO 294/4 |
Mechanical Properties
| Propriedade | Valor | Norma | Método |
|---|---|---|---|
| Tensile Strength at Yield | 48 MPa | 50mm/min | ISO 527 |
| Tensile Elongation at Break | 15 % | 50mm/min | ISO 527 |
| Tensile Modulus | 2300 MPa | 1mm/min | ISO 527 |
| Flexural Strength | 75 Mpa | 2mm/min | ISO 178 |
| Flexural Modulus | 2300 MPa | 2mm/min | ISO 178 |
| Notched Izod Impact Strength | 19 kJ/m² | 23℃,5.5J | ISO 180/1A |
Thermal properties
| Propriedade | Valor | Norma | Método |
|---|---|---|---|
| Vicat Softening Temperature | 102 ℃ | 50N, 50℃/h | ISO 306 |
| Heat Distortion Temperature | 82 ℃ | 1.8MPa | ISO 75-2/A |
As informações de fornecedores e gamas fornecidas neste website destinam-se apenas a referência de indexação do setor. Não somos agentes oficiais de nenhuma marca de terceiros e o conteúdo exibido não constitui uma oferta de venda nem uma relação de agência. A autenticidade, o preço e a disponibilidade do produto estão sujeitos ao fornecedor real.