PA12 SLS Interlayer Peeling
Fenómeno del problema
【Problem phenomenon】SLS printed PA12 parts had weak interlayer bonding and cracked along layers under stress
Análisis de la causa
Insufficient temperature or too-fast scanning makes interlayer fusion inadequate; when the interlayer temperature gradient is large, the new layer cannot fully diffuse and bond with the solidified layer; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
Solución
Increase preheating temperature and laser energy input; reduce scanning speed to extend melting time; optimize layer thickness and placement direction to reduce thermal stress; after adjustment, take consecutive samples to verify the effect, and resume mass production only after confirming stability
Conclusión clave
Interlayer peeling is a signal of insufficient energy; raise temperature and reduce speed to promote interlayer fusion; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a reference for troubleshooting similar problems in the future