Blow Molding
8 visualizaciones
CEF extrusion '2079851475616104457 parison sag severe
Fenómeno del problema
CEF extrusion '2079851475616104457 parison sag 20-40mm, resulting in bottle bottom wall thickness only 0.3-0.4mm
Análisis de la causa
CEF melt strength low, parison stretches and thins under gravity; slow parison extrusion speed increases sag time; parison temperature too high, low viscosity aggravates sag
Solución
1) Add micro-crosslinking agent 0.3-0.5wt% to improve melt strength; 2) Increase parison extrusion speed to shorten sag time; 3) Lower parison temperature by 10-15°C to increase viscosity; 4) Wall thickness controller to compensate sag
Conclusión clave
Parison sag is caused by low melt strength, micro-crosslinking and wall thickness control are key