Product defects caused by poor drying of high impact polystyrene raw material

Raw '2079851475616104451 is the basic process to ensure product quality.

Material Drying raw '2079851475616104451moisture contentsilver streakbubblesdehumidifying dryer

Poor electroplating adhesion of high impact polystyrene ABS products

ABS electroplating quality is closely related to material grade and internal stress.

Thermoforming electroplating adhesionABSinternal stresselectroplating grademold release agent

Uneven surface of high impact polystyrene extruded profiles

Extrusion & Post uneven surfaceprofilehigh impact polystyreneextrusion moldingsurface quality

Annealing treatment of high impact polystyrene products to improve stress

Annealing treatment is an effective method to reduce product residual stress.

Extrusion & Post annealingresidual stressheat deflection temperaturedimensional stabilitystress cracking

Insufficient weather resistance/yellowing of high impact polystyrene ASA products

Material Analysis weather resistanceyellowingASAultravioletprocessing temperature

Burnt marks in the slider area of high impact polystyrene injection products

Thermoforming burnt marksslider areahigh impact polystyrene'2079851475616104452process optimization

Surface Static Electricity Problem of general purpose polystyrene Products

The static electricity problem is caused by the high insulation of the material.

Molding Process static electricityantistatic agentvolume resistanceambient humiditysurface treatment

Insufficient Welding/Fusion Strength of general purpose polystyrene Products

The welding strength is determined by the melt fusion quality.

Material Drying welding strengthwelding temperaturewelding pressuresurface cleaningmelt fusion

Dimensional Change with Temperature/Thermal Expansion of general purpose polystyrene Products

Production & Quality thermal expansiondimensional changetemperature influencethermal expansion coefficientdesign compensation

Shrinkage Rate Prediction Deviation of general purpose polystyrene Products

Molds & Tooling shrinkage ratemold designwall thickness influenceflow directionmold trial verification