Material Drying
4 조회수
Control of LCP Regrind Usage Ratio
문제 현상
【Problem Phenomenon】After blending in regrind, the soldering blistering rate of LCP products rises and strength decreases
원인 분석
After regrind has experienced thermal history, its molecular weight decreases and it may absorb moisture; when the ratio is too high, both soldering heat resistance and strength decrease; LCP regrind control is a common topic in mass production of high-temperature soldered parts
해결 방법
Strictly control the regrind ratio for soldered parts and verify the oil bath blistering rate; dry regrind separately before use; establish regrind batch traceability and performance sampling inspection; after adjustment, take continuous samples to verify the effect, and resume mass production only after confirming stability
핵심 요약
LCP regrind must be re-dried and its ratio limited; soldered parts require strict verification; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar problems
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!