Molding Process
4 조회수
PA6 Warpage
문제 현상
Product warpage deformation, obvious on flat parts, with uneven assembly gaps.
원인 분석
PA6 shrinkage is 1.5%~2.5% and the difference between flow/transverse shrinkage is large; uneven cooling, improper holding pressure, and differential shrinkage caused by molecular orientation all cause warpage; the anisotropy of crystalline materials is the root cause.
해결 방법
①Balance mold temperature (separate-circuit temperature control) to reduce temperature difference;②optimize the holding pressure curve, taking into account both compensation and internal stress;③optimize wall thickness uniformity to reduce differential shrinkage;④constrain flat parts with setting fixtures after demolding;⑤optimize gate position to improve material flow and confluence.
핵심 요약
PA6 warpage = 'high shrinkage + orientation': setting fixtures are a sharp tool; warpage of crystalline materials requires balancing mold temperature, restraining holding pressure, and constraining setting in three ways, and the setting constraint after demolding is especially effective.
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!