PA66 thick-walled part mold temperature
문제 현상
PA66 thick-walled structural parts internal shrinkage voids, X-ray inspection unqualified
원인 분석
When thick-walled part mold temperature is low, the surface layer solidifies first, the core feeding channel freezes forming shrinkage voids; holding pressure cannot penetrate the solidified layer; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based solely on experience
해결 방법
Raise thick-walled part mold temperature to 100-120℃ to delay solidification; thicken the gate to keep the feeding channel; holding pressure and time calculated by wall thickness; after adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability
핵심 요약
Thick-wall shrinkage voids are solved by high mold temperature plus effective feeding channels; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar problems
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!