Molds & Tooling
2 Aufrufe
PA66 thick-walled part mold temperature
Problembeschreibung
PA66 thick-walled structural parts internal shrinkage voids, X-ray inspection unqualified
Ursachenanalyse
When thick-walled part mold temperature is low, the surface layer solidifies first, the core feeding channel freezes forming shrinkage voids; holding pressure cannot penetrate the solidified layer; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based solely on experience
Lösung
Raise thick-walled part mold temperature to 100-120℃ to delay solidification; thicken the gate to keep the feeding channel; holding pressure and time calculated by wall thickness; after adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability
Wichtigste Erkenntnis
Thick-wall shrinkage voids are solved by high mold temperature plus effective feeding channels; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar problems
War das hilfreich?
0 Personen fanden dies hilfreich
Vielen Dank für Ihr Feedback!