PA66 low-temperature impact shortcoming
문제 현상
PA66 parts used in cold regions fracture brittlely at low temperature, yet the same grade passes testing at normal temperature
원인 분석
PA66 low-temperature impact performance is inferior to PA6, and brittleness is significant under the dual action of dry state and low temperature; if cold-region applications are designed according to normal-temperature data, hidden dangers of batch failure will be left
해결 방법
①Perform low-temperature impact verification for cold-region applications; ②Select toughened modified grades or evaluate PA6 substitution; ③Low-temperature performance of products improves after moisture conditioning; after adjustment, take continuous samples to verify the effect, confirm stability before resuming mass production
핵심 요약
The shortcoming of PA66 is at low temperature; cold-region applications must be verified at low temperature, toughened grades or PA6 substitution are the two ways out; after confirming effectiveness, fix the parameters and practices into the work instructions to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!