PA66 low-temperature impact shortcoming
Fenómeno do problema
PA66 parts used in cold regions fracture brittlely at low temperature, yet the same grade passes testing at normal temperature
Análise das causas
PA66 low-temperature impact performance is inferior to PA6, and brittleness is significant under the dual action of dry state and low temperature; if cold-region applications are designed according to normal-temperature data, hidden dangers of batch failure will be left
Solução
①Perform low-temperature impact verification for cold-region applications; ②Select toughened modified grades or evaluate PA6 substitution; ③Low-temperature performance of products improves after moisture conditioning; after adjustment, take continuous samples to verify the effect, confirm stability before resuming mass production
Conclusão principal
The shortcoming of PA66 is at low temperature; cold-region applications must be verified at low temperature, toughened grades or PA6 substitution are the two ways out; after confirming effectiveness, fix the parameters and practices into the work instructions to prevent recurrence