PC Internal Stress Cracking
문제 현상
[Problem Phenomenon] PC products crack after storage or assembly, caused by internal stress
원인 분석
PC's rigid molecular chains make internal stress difficult to eliminate; low mold temperature, high holding pressure, uneven cooling and wall thickness transitions all aggravate it; internal stress is released and cracks under solvents or loads; when troubleshooting on site, verify each item according to this mechanism one by one, and avoid blindly adjusting the machine based on experience alone
해결 방법
High mold temperature and low holding pressure to reduce stress; uniform wall thickness; annealing to relieve stress; polariscope stress detection; after adjustment, take samples continuously to verify the effect, and resume mass production only after confirming stability; change only one variable at a time and record parameter changes, so as to locate effective measures
핵심 요약
PC internal stress is the culprit of cracking; high mold temperature, annealing and polariscope detection; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a reference for troubleshooting similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!