PEI Internal Stress Cracking
문제 현상
PEI products generate internal stress during cooling, leading to deformation or cracking; cracks mostly originate from sharp corners and assembly stress points.
원인 분석
PEI's glass transition temperature is as high as 217℃, and fast cooling freezes molecular chains with large stress; excessive cooling speed or unreasonable mold design accumulates internal stress; unreleased stress triggers cracking during use.
해결 방법
①Use a high-temperature mold with mold temperature of 140~180℃ to reduce internal stress; ②sufficient cooling time but avoid overcooling; ③eliminate sharp corners in the structure with rounded transitions; ④anneal when necessary.
핵심 요약
PEI internal stress management revolves around high mold temperature; the 217℃ Tg determines the process temperature level; structural rounded corners are the design bottom line.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!