PET sheet edge cracking
문제 현상
Edge cracks in the sheet, tearing during winding, and frequent production interruptions
원인 분석
Improper cooling creates excessive internal stress in the sheet; degraded material has insufficient toughness; excessive winding tension strains the edges; uneven thickness makes edges locally too thin; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
해결 방법
① Optimize cooling conditions to reduce internal stress; ② improve raw material quality; ③ adjust winding tension and keep thickness consistent; after adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability
핵심 요약
PET sheet edges are weak zones of stress and thickness; a three-pronged approach of cooling, tension, and thickness prevents edge cracking and web breaks; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!