Problembeschreibung
Edge cracks in the sheet, tearing during winding, and frequent production interruptions
Ursachenanalyse
Improper cooling creates excessive internal stress in the sheet; degraded material has insufficient toughness; excessive winding tension strains the edges; uneven thickness makes edges locally too thin; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
Lösung
① Optimize cooling conditions to reduce internal stress; ② improve raw material quality; ③ adjust winding tension and keep thickness consistent; after adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability
Wichtigste Erkenntnis
PET sheet edges are weak zones of stress and thickness; a three-pronged approach of cooling, tension, and thickness prevents edge cracking and web breaks; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
War das hilfreich?
0 Personen fanden dies hilfreich
Vielen Dank für Ihr Feedback!