Molds & Tooling
4 조회수
POM Shrinkage Rate 1.8-3.5%
문제 현상
Large dimensional deviation of the part, shrinkage voids and sink marks in thick-walled areas, and inconsistent shrinkage at different wall thicknesses in the same mold
원인 분석
POM has high crystallinity; when transitioning from melt to crystalline solid, the shrinkage rate is 1.8-3.5% and shrinkage is greater at thick walls; wall thickness differences cause density differences, and thick-wall melt flowing toward thin walls aggravates non-uniformity
해결 방법
①Allow margin in the mold according to shrinkage rate and correct through mold trials; ②make wall thickness as uniform as possible; ③strengthen holding pressure feeding for thick-walled parts to prevent shrinkage voids; after adjustment, take continuous samples to verify the effect, and resume mass production only after confirming stability
핵심 요약
POM's shrinkage ranks among the highest in engineering plastics; uniform wall thickness, holding pressure compensation, and mold margin allowance are the three key elements of dimensional control; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!