Molds & Tooling
4 조회수
Poor PVA fatigue resistance
문제 현상
PVA product fatigue life <10⁴ cycles, below the 10⁵ cycle requirement
원인 분석
PVA elastic recovery insufficient, each cycle accumulates plastic deformation; crosslinking degree on the low side, fatigue cracks propagate fast
해결 방법
1) Increase crosslinking degree to improve recovery and reduce accumulated deformation; 2) Select high molecular weight grade to raise the fatigue threshold; 3) Product design to reduce stress concentration
핵심 요약
Poor fatigue resistance is caused by insufficient recovery and fast crack propagation; increasing crosslinking is the key