Poor PVA fatigue resistance
Fenómeno del problema
PVA product fatigue life <10⁴ cycles, below the 10⁵ cycle requirement
Análisis de la causa
PVA elastic recovery insufficient, each cycle accumulates plastic deformation; crosslinking degree on the low side, fatigue cracks propagate fast
Solución
1) Increase crosslinking degree to improve recovery and reduce accumulated deformation; 2) Select high molecular weight grade to raise the fatigue threshold; 3) Product design to reduce stress concentration
Conclusión clave
Poor fatigue resistance is caused by insufficient recovery and fast crack propagation; increasing crosslinking is the key