Injection Molding
3 조회수
DSTDP injection severe flash
문제 현상
DSTDP injection molded product parting line flash 0.05-0.1mm wide >2mm, requiring secondary trimming
원인 분석
Injection pressure too high >80MPa, melt overflows from the parting line; clamping force insufficient; mold parting line fitting gap >0.02mm
해결 방법
1) Reduce injection pressure to 60-70MPa; 2) increase clamping force or use a larger tonnage injection machine; 3) mold fitting gap <0.02mm; 4) increase melt viscosity to reduce mold penetration tendency
핵심 요약
Flash is caused by high-pressure injection and mold gap; reducing pressure and improving mold fitting are key