Longitudinal reversion of homopolymer polypropylene pipes exceeding standard
문제 현상
After the pipe is heated under specified temperature and time conditions, the longitudinal reversion exceeds the standard limit.
Excessive reversion reflects large internal stress or incomplete crystallization of the pipe, affecting pipe use reliability.
원인 분석
(1) Large residual internal stress in homopolymer polypropylene after extrusion
(2) Cooling rate too fast; molecular chain orientation not relaxed
(3) Haul-off speed too high; excessive longitudinal stretching of the pipe
(4) Barrel temperature too low, insufficient melt plasticization
(5) Insufficient sizing cooling
해결 방법
(1) Appropriately increase barrel temperature to a reasonable value within the 200-280°C range, improve plasticization
(2) Appropriately reduce cooling rate, allow molecular chains relaxation time
(3) Adjust haul-off speed, reduce draw ratio
(4) Increase cooling water tank length, ensure full cooling
(5) Perform water bath annealing after pipe demolding to eliminate internal stress
핵심 요약
Excessive reversion is caused by large internal stress or excessive orientation; it needs to be solved from temperature control, cooling rate, and haul-off speed.