문제 및 해결책

일반적인 플라스틱 재료 문제에 대한 실질적인 답변

기사 둘러보기 →

Q

PA6 Ultrasonic Welding Strength

A

PA6 welding quality is strongly related to moisture state, and unified material state is the premise; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence

Material Drying PA6 ultrasonic welding weld conditioning

Q

PA6 Hydrolysis Aging

A

High-temperature water contact is a sensitive service condition for PA6, and hydrolysis-resistant grades are a necessary choice; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence

Material Drying PA6 hydrolysis coolant pipe hydrolysis resistance

Q

PA6 Creep Stress Relaxation

A

PA6 long-term load-bearing design must be checked according to creep characteristics and cannot apply short-term strength; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence

Material Drying PA6 creep stress relaxation long-term load

Q

PA6 Dry-State Embrittlement

A

Dry-state embrittlement is an inherent property of PA6, and conditioning is the most effective toughness restoration means; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence

Material Drying PA6 dry-state embrittlement conditioning toughness

Q

PA6 Dimensional Stability After Conditioning

A

The conditioned state is the real service state of PA6, and the inspection benchmark must be unified; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for s...

Material Drying PA6 conditioning dimensional benchmark inspection

Q

PA6 Water Absorption Dimensional Change

A

PA6 dimension management must consider moisture expansion, and inspection is only valid after conditioning; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference...

Material Drying PA6 moisture expansion dimensional change conditioning

Q

PA6 Yellowing Overheating Identification

A

For yellowing, first distinguish whether overheating is in the drying stage or the molding stage, then reduce temperature accordingly; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as ...

Material Drying PA6 yellowing thermal oxidation residence

Q

PA6 Silver Streaks and Bubbles Differentiation

A

Silver streak treatment first distinguishes the cause, and air shot observation is the fastest identification means; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting ...

Material Drying PA6 silver streak bubble air shot identification

Q

PA6 Bubble Cause Differentiation

A

Classifying and characterizing PA6 bubbles is the premise of rectification; the three routes of water vapor, vacuum and degradation must not be confused, test first before acting; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence

Material Drying PA6; bubble; vacuum void; degradation; classification troubleshooting

Q

PA6 Silver Streaks Dominated by Moisture

A

When PA6 shows silver streaks, suspect drying first rather than the process; the three checks of dew point, moisture content and re-humidification save the time of trial-and-error machine adjustment; after confirming effectiveness, solidify the parameters and practices into the work instruction t...

Material Drying PA6; silver streak; moisture; dew point; -30°C