Insufficient clamping force

The mold is forced open by the transfer pressure causing flash. When this defect appears in products of Process No. 4, it is usually related to a specific process parameter range or equipment state. If it continues to appear, it will directly affect the product qualification rate and production rhythm, increasing material loss and rework costs. Timely diagnosis and elimination is a basic requirement for ensuring stable production.

1. Process parameter factors: hydraulic system clamping force insufficient, clamping force set too low, large mold area and high transfer pressure. 2. Runner and gate design factor: In transfer molding, the material needs to enter the cavity through runners and gates; the runner length, cross-sectional shape and gate size directly affect pressure loss, fiber breakage and filling balance, and unreasonable design is the root of many quality problems. 3. Feeding factor: The volume of the feeding chamber, the feeding amount and the preheating state of the material directly determine the transfer pressure and filling effect, and are key variables unique to transfer molding.

1. Process parameter optimization and adjustment: increase the clamping force setting, overhaul the hydraulic system, match the clamping force with the transfer pressure (the clamping force should be greater than the transfer pressure × the product projected area). 2. Systematic troubleshooting method: Troubleshooting of transfer molding problems follows the order of 'runner -> feeding -> parameters -> mold'. First check whether the runners and gates are blocked or worn, then verify the feeding amount and material preheating, then adjust the transfer pressure and speed, and finally check the mold venting and temperature uniformity. 3. Preventive management: Establish standardized process parameter cards and quality control limits for each set of mold/product, and regularly conduct process capability index (CPK) evaluations. For recurring problems, use fishbone diagrams or 5Why analysis to trace the root cause, and solidify the countermeasures as PFMEA control points.

This problem is a typical manifestation of insufficient clamping force in transfer molding; the core of the solution lies in the rational design of the runner and gate system, the effective transmission of transfer pressure, and the uniform control of mold temperature. It is recommended to start troubleshooting from the runner system and transfer parameters.