Extrusion & Post
8 views
EAA internal delamination cracking
Problem Phenomenon
EAA products delaminated internally, cracking along the interface
Cause Analysis
Poor interfacial bonding between EAA and incompatible fillers or blend components; cooling shrinkage difference causing interlayer stress
Solution
1) Use compatibilizer to improve interfacial bonding; 2) Uniform cooling to reduce interlayer stress; 3) Reduce the addition amount of incompatible components
Key Takeaway
Internal delamination is caused by poor interface and shrinkage difference; compatibilizer and uniform cooling are key